WPC door frames are made of 70% Virgin Polymer, 15% Wood Powder and 15% Additives that strengthens it to withstand any composition of a door, irrespective of its size, weight, and density . WPC door frames provide can hang any type of door like MS doors, FRP doors, or even SS doors. This is only possible because the core density is versatile.
It has a high nail - holding strength of 2200N and a density of 1100 kg/m 3 . The WPC door frames are available in standard sections of 75”x45 ”, 100”x50”, 100”x60”, 125”x50”, 125”x60”, 150”x50” and 150”x60”. The length of the door frames available is 3.5’, 7.5’, 8.5’ and 12’. These door frames provide door operation for years and are easy to work with. It has wide applications in commercial buildings , residential bung a lows and apartments etc.
Certified under Forest Stewardship Council
IGBC -> Indian Green Building Council. IGBC is the accreditation agency for LEED rating in India.
E-1 CERTIFIED Bhutan Tuff products are Low Formaldehyde Emission (LFE) certified OHSAS 18001 Certified
JAS-ANZ CERTIFIED ISO-9001:2000 Certified Company
ISI CERTIFIED Bhutan Tuff products are made under strict BIS Standards (Bureau of Indian Standard) an Indian Government Body.
ISO 14001 Certified for Quality Management System
OHSAS 18001 Certified for Quality Management System Standard
Make in India
Technical Specification
| Tests | Results | Protocol |
| Desnsity,Kg/m^3 | 567 | IS:2380 (Part III)- 1997 Reaffirmed 2013 |
| Moisture content, % | 0.14 | IS:2380 (Part III)-1997 Reaffirmed 2013 |
| Water Absorption % (i) For 2 hrs soaking (ii) For 24 hrs soaking |
0.08 0.09 |
IS:2380 (Part XVI)-1997 Reaffirmed 2013 |
| Thickness Swelling, % (For 2 hrs) | 0.05 | IS:2380 (Part- XVII) -1997 Reaffirmed 2013 |
| Modulus of Rupture, N/mm2 | 25.2 | IS:2380 (Part-IV)-1997 Reaffirmed 2013 |
| Modulus of Elasticity, N/mm2 | 1989 | IS:2380(Part-IV)-1997 Reaffirmed 2013 |
| Tensile Strength, MPa | 1.30 | IS:2380(Part-VI)-1997 Reaffirmed 2013 |
| Screw Withdrawal Strength, N (A) Face (b)Edge |
1267 698 |
IS:2380 (Part XIV)-1997 Reaffirmed 2013 |
| Nail Withdrawal Strength, N | 243 | IS:2380 (Part XIV)-1997 Reaffirmed 2013 |
| Shock Resistance Test, 5 Kgf | Not Applicable on this product | IS:4020 (Part 7)-1998 Reaffirmed 2008 |
| Water Resistance Test (at 60±2ᴼ C for 3hrs) |
No deformation is observed | IS:1734 (Part 6)-1998 Reaffirmed 2013 |
| Knife Test | Passes the test | IS:4020 (Part 14)-1998 Reaffirmed 2008 |
| Resistance to steam | Passes the Test | IS:12823: 1990 (Reaffirmed 2015) |
| Resistance to crack | Passes the Test | IS:12823: 1990 (Reaffirmed 2015) |
| Resistance to cigarette burn | Passes the Test | IS:12823: 1990 (Reaffirmed 2015) |
| Resistance to stain (i)Coffee (ii) Acetic acid |
Passes the Test | IS:12823: 1990 (Reaffirmed 2015) |
| Humidity Test (Varying) Condition I: At 27±2 c % 30±5% Relative Humidity for one week (a)Leangth (b)Width (c)Thickness (d)Diagonal Condition 2: At 27±2 C% 85±5% Relative Humidity for one week (a)Length (b)Width (c)Thickness (d)Diagonal |
Passes the Test | IS:4020 (Part 12)-1998 Reaffirmed 2008 |
| Thickness,mm | 18.8 | IS:2380 (Part II)-1997 Reaffirmed 2013 |
| Edge Straightness test, mm | 0.4 | IS:2380 (Part II)-1997 Reaffirmed 2013 |
| Squareness,mm | Nil | IS:2380 (Part II)-1997 Reaffirmed 2013 |
| Workability | Satisfactory | ……. |