Doors offer safety and privacy hence, only an elegant look is not sufficient. Wood Polymer Composite (WPC) is an emerging material in the building material industry. Without a doubt, it has been a remarkable substitute of all conventional door materials such as wooden or steel doors that have been used in past decades. We manufacture high-quality doors in many trendy options. Bhutan Tuff is a well-known brand where you can get both, beauty and quality doors. Being 100% eco-friendly, WPC doors are an emerging alternative solution that is highly demanded by architects to be used in high-class projects and designs. WPC doors can be cut easily with minimum effort and no hassles. Screwing on WPC doors is highly recommended. It is very good for Hinges, the fixation of hinges on WPC doors can be carried out simply. WPC doors are compatible with any type of locks.
These are available in 2 variants Low density and High density respectively. There are more than 500 veneer designs for the WPC doors. It comes in standard widths of 27, 30, 33, 37 and 39 and thicknesses of 25mm, 30mm and 35mm as per orders.
Certified under Forest Stewardship Council
IGBC -> Indian Green Building Council. IGBC is the accreditation agency for LEED rating in India.
E-1 CERTIFIED Bhutan Tuff products are Low Formaldehyde Emission (LFE) certified OHSAS 18001 Certified
JAS-ANZ CERTIFIED ISO-9001:2000 Certified Company
ISI CERTIFIED Bhutan Tuff products are made under strict BIS Standards (Bureau of Indian Standard) an Indian Government Body.
ISO 14001 Certified for Quality Management System
OHSAS 18001 Certified for Quality Management System Standard
Make in India
Technical Specification
| S.No | Tests | Results | Protocol |
| 1 | Desnsity,Kg/m^3 | 567 | IS:2380 (Part III)- 1997 Reaffirmed 2013 |
| 2 | Moisture content, % | 0.14 | IS:2380 (Part III)-1997 Reaffirmed 2013 |
| 3 | Water Absorption % (i) For 2 hrs soaking (ii) For 24 hrs soaking |
0.08 0.09 |
IS:2380 (Part XVI)-1997 Reaffirmed 2013 |
| 4 | Thickness Swelling, % (For 2 hrs) | 0.05 | IS:2380 (Part- XVII) -1997 Reaffirmed 2013 |
| 5 | Modulus of Rupture, N/mm2 | 25.2 | IS:2380 (Part-IV)-1997 Reaffirmed 2013 |
| 6 | Modulus of Elasticity, N/mm2 | 1989 | IS:2380(Part-IV)-1997 Reaffirmed 2013 |
| 7 | Tensile Strength, MPa | 1.30 | IS:2380(Part-VI)-1997 Reaffirmed 2013 |
| 8 | Screw Withdrawal Strength, N (A) Face (b)Edge |
1267 698 |
IS:2380 (Part XIV)-1997 Reaffirmed 2013 |
| 9 | Nail Withdrawal Strength, N | 243 | IS:2380 (Part XIV)-1997 Reaffirmed 2013 |
| 10 | Shock Resistance Test, 5 Kgf | Not Applicable on this product | IS:4020 (Part 7)-1998 Reaffirmed 2008 |
| 11 | Water Resistance Test (at 60±2ᴼ C for 3hrs) |
No deformation is observed | IS:1734 (Part 6)-1998 Reaffirmed 2013 |
| 12 | Knife Test | Passes the test | IS:4020 (Part 14)-1998 Reaffirmed 2008 |
| 13 | Resistance to steam | Passes the Test | IS:12823: 1990 (Reaffirmed 2015) |
| 14 | Resistance to crack | Passes the Test | IS:12823: 1990 (Reaffirmed 2015) |
| 15 | Resistance to cigarette burn | Passes the Test | IS:12823: 1990 (Reaffirmed 2015) |
| 16 | Resistance to stain (i)Coffee (ii) Acetic acid |
Passes the Test | IS:12823: 1990 (Reaffirmed 2015) |
| 17 | Humidity Test (Varying) Condition I: At 27±2 c % 30±5% Relative Humidity for one week (a)Leangth (b)Width (c)Thickness (d)Diagonal Condition 2: At 27±2 C% 85±5% Relative Humidity for one week (a)Length (b)Width (c)Thickness (d)Diagonal |
Passes the Test | IS:4020 (Part 12)-1998 Reaffirmed 2008 |
| 18 | Thickness,mm | 18.8 | IS:2380 (Part II)-1997 Reaffirmed 2013 |
| 19 | Edge Straightness test, mm | 0.4 | IS:2380 (Part II)-1997 Reaffirmed 2013 |
| 20 | Squareness,mm | Nil | IS:2380 (Part II)-1997 Reaffirmed 2013 |
| 21 | Workability | Satisfactory | ……. |